  The TAC film for insulation, produced with triacetate cellulose and plasticizer ,resolved in the methylene chloride into dope, through casting,drying and winding process, is mainly used as insulation separate film for aero battery with thickness of 30μm \ 40μm .
  TAC department has set up its own R&D center which provides continuous technical support for improving the quality of the TAC film insulation application.The modern production and management system ensure the high quality products with thickness of 30μm \ 40μm .
Data

Item
Unit
Insulation film
Thickness
μm
30±2 \ 40±2
Thickness tolerance
μm
8
Light transmittance
%
90
Breaking strength
MPa
60
Breaking elongation
%
30
Shrinkage ratio
Machine direction
%
0.5
Cross Direction
0.5
Additional: 
Label, packing , storage and transportation . 
Packing: The clear plastic bag is used for the damp proof purpose , the Roll was suspended supported by frame.

Storage :storage with a temperature.(21--23)℃, Relative Humidity not more than 65%, sun proof, over 1m away from the heating resource , the guarantee period since delivery : 1 year
Label, packing ,storage and transportation .

Label: Labels are attached to all the quality products with following information : Name, Trade mark, Model No. specs, Length, serial No. Making No. , Date , Manufacturer, Address as well as the product identification No. outside the packing are printed “ damp proof , sun proof , shock proof. ”
Transportation : Sun , rain and shock proof during transportation.
Contact us for Tac film products:
Sales Manager:  Mr. Sun Zhen or Mr. Kang shuan
Tel:  0086-312-3302738
Sales Department of TAC fim
Questionnaire Survey | Contacts US | Purchasing on Line |  
Phone :0086-312-7923000             Fax:0312-7923001
The ISO9001&ISO14000 attestation passed     Copyright 2010 Lucky Film Corp.. All rights reserved.